Search results for "Aisi 316l"
showing 5 items of 5 documents
Effect of E. coli biofilm formation and removal on passive films on AISI 316L during fermentation processes
2021
Abstract 316L coupons were sanitized in hot water vapour inducing iron enrichment in passive films. Coupons were then immersed in a pilot fed-batch fermenter in presence of E. coli. Sanitization causes iron enrichment in passive films. Fermentation causes the growth of biofilm on the SS, constituted by bacteria embedded in an extracellular polymeric substance. During fermentation SS open circuit potential is very negative due to low oxygen concentration on its surface, while the chelating action of siderophores induces chromium enrichment in the passive film. Disinfection in NaClO for 30 min allows removal of biofilm and formation of a protective passive film.
Photoelectrochemical monitoring of rouging and de-rouging process on AISI 316L for chemical reactors
2016
The food and fine-chemical industry has for a long time been troubled by red brown to dark violet deposits in distillation columns, storage vessels and distribution systems for purified water and clean steam. Owing to the visual appearance of those deposits, the phenomena was referred as rouge. Although formation of rouge, i.e. rouging, is a commonly known phenomenon in stainless steel systems, the basic mechanism is still not fully understood. The phenomenon causes precipitation of iron as fine red-brown ferric oxide or hydroxide particles. Moreover adherent discoloration of the stainless steel surface is often observed in conjunction with the loosely adhered rouge particles. The affected …
Study of Passive Films Formed on AISI 316L Stainless Steel in Non-Polluted and Underwater-Volcano-Polluted Seawater
2014
This work studies the semiconducting behavior of passive films formed on AISI 316L (UNS S31603) in two different sea-water solutions, non-polluted and polluted, collected from the volcano of El Hierro Island. Polarization measurements, potentiostatic passivation tests, electrochemical impedance spectroscopy, and capacitance measurements were performed. Results show that the polluted seawater worsens passivation kinetics. Additionally, passive films formed on AISI 316L stainless steel in polluted seawater have been found to be less protective than those formed in non-polluted seawater, showing a more defective structure, owing to the acidity of the polluted medium.
Additive manufacturing, new elaboration technique of metallic materials : impact of the microstructure on high temperature durability of AISI 316L st…
2021
Additive Manufacturing (AM) processes are able to elaborate, in a single step, metallic parts with very complex geometry, as close as possible to their final dimensions, based on 3D CAD model. Despite a very large number of studies on AM parameters, very few studies report on the high temperature behavior of the metallic materials produced by these processes. This thesis work evaluates the impact of the Selective Laser Melting (SLM) process on the high temperature durability of the austenitic stainless steel AISI 316L, commercial grade widely used in the industry. For this purpose, the reactivity of SLM samples was studied in different conditions (atmosphere, temperature, isothermal or cycl…
Galvanic Deposition of Calcium Phosphate/Bioglass Composite Coating on AISI 316L
2023
Calcium phosphate/Bioglass composite coatings on AISI 316L were investigated with regard to their potential role as a beneficial coating for orthopedic implants. These coatings were realized by the galvanic co-deposition of calcium phosphate compounds and Bioglass particles. A different amount of Bioglass 45S5 was used to study its effect on the performance of the composite coatings. The morphology and chemical composition of the coatings were investigated before and after their aging in simulated body fluid. The coatings uniformly covered the AISI 316L substrate and consisted of a brushite and hydroxyapatite mixture. Both phases were detected using X-ray diffraction and Raman spectroscopy.…